Photoimageable Curable Solder Thermal Curable Marking Ink , Black PCB Printing Ink

Good quality PCB Marking Ink for sales
Good quality PCB Marking Ink for sales
Thanks for your support always .After a long time testing and adjusting ,we finally get the perfect ink from you. Cheers.

—— Kalpesh Patel

We have received 3 times sample by your side in last 3 months .Appreciated your hard work and patience . Wait for your first shipment arrival.

—— Dzmitry Anoshka

I like your green solder mask pcb ink ,especially dark shinning green !

—— Mohsen Esmaeili

It is the first time we buy from China .Everything is fine and thanks for your invitations to leave message on your website.

—— Vũ Trang

I'm Online Chat Now

Photoimageable Curable Solder Thermal Curable Marking Ink , Black PCB Printing Ink

China Photoimageable Curable Solder Thermal Curable Marking Ink , Black PCB Printing Ink supplier

Large Image :  Photoimageable Curable Solder Thermal Curable Marking Ink , Black PCB Printing Ink

Product Details:

Place of Origin: China
Brand Name: NUOJINSEN
Certification: ROHS,SGS
Model Number: 73737

Payment & Shipping Terms:

Minimum Order Quantity: 100kgs
Price: Negotiation
Packaging Details: 1kg,5kg,10kg,20kg
Delivery Time: 7-10days
Payment Terms: T/T,LC
Supply Ability: 100000kgs/month
Detailed Product Description
Color: Black Fineness: ≤8µm
Mix Ratio: Base/Hardener=3:1 Solid Content After Mixing: 75±3%
Viscosity After Mixing (25℃): 200±30 DPa﹒s Density After Mixing (25℃): 1.30 ~1.50 G/ml
Pot Life After Mixing: 24 Hour Environment Standard: In Compliance With RoHS Directives
Halogen Content: ≤600ppm Pre-baking: 75℃ , 70 Min
Exposure Energy: 300 ~600 MJ/cm2 Shelf Life: 6 Months Since The Date Of Manufacture
High Light:

uv curable pcb ink

,

liquid solder mask

Black color pcb ink,photoimageable curable solder resist mask

 

 

Working procedure

1. Mixing

Mixing a small amount main agent with hardener and stirring thoroughly,then mixing the mixture above with the remanent main agent,add appropriate diluent and stirring 5-10 minutes. The viscosity of ink is adjusted to 120 PS if printed by hand. And it is adjusted to 180 PS if printed by machine.It is adjusted to 200 PS if it is aluminum tamponade .The viscosity of ink mixed above is measured at 25 degrees. Please use the special diluent of our company if the viscosity of ink needs to adjust.

  • Remain time

10-15 minutes after stiring uniformly

  • Ordinary boards:43T;Chemical-plating Aurum or Tin boards:36T
  • Pre-baking

1) Single side printing separately

First side:72-76 degrees,15-18 min

Second side:72-76 degrees,30-35 min

  • Double sides printing simultaneously:72-76 degrees,40-60min
  • Exposure

300-500mJ/cm2,Black ink:600-750mJ/cm2,exposure step:10-12 steps

  • Developing:
  • Photoimageable Curable Solder Thermal Curable Marking Ink , Black PCB Printing Ink

Developing solution:0.8-1.2wt% Na2CO3 or K2CO3 aqueous solution

Developing solution temperature:28-32 degrees

Spray pressure:1.5-2.5kg/cm2

Developing time:40-90 seconds

  • Post cure

Spray Tin board:150 degrees*(60-120min)

Chemical-plating Aurum board:150 degrees*(50-60min)

Thick copper plate,boards printed with black ink should be post-black in subsection:75 degrees*(60-120min)+100 degrees*30 min+150 degrees*(60-90min)

  • Safe time

6 months since the date of manufacture,store below 25 degree in dark

  • Attention:

1) Mixing the ink fully before using

2) We will offer you special diluent or PMA if the ink need dilute

3) The values above are based on experiments in our lab.Experiments need to be carried out in order to get proper using condition.

 

1.Service

A.You can get the competitive price with high quality
B. We focus on the product material to use different stuff.
C.We teach customers to improve the production time.Help customers development the new process.